I spent the past few days throwing a large amount of test tiles using 3 different cone 6 bodies to test both in cone 6 oxidation and soda. Can someone please share their cone 6 oxidation schedule for me to test both the SH glazes and my own cone 6 calcium matts and other glazes.

Stevens higher cone firing schedule is on his page, but not the cone 6. From what I have garnered reading some messages on the group, the schedule is  6 to cone 6 1/2, hold 1 hr, fast drop to 1600. Is there a hold at 1600? Also, is this the correct schedule? My tiny test kilns are manual and my bisque electric kiln is pretty big, so I don't want to waste all the work throwing, trimming and glazing around 100 tiles for the C6 ox firing, by not using the right firing schedule.

 

Thanks for any help!

June

http://www.shambhalapottery.com

http://www.shambhalapottery.blogspot.com

 

Views: 5722

Replies to This Discussion

Hi June ~

I have the schedule, but it's at the studio and it's only 8:30 am here...
I'll post it for you when I go into work today about 11:00.. If you haven't gotten it before that..

~ Tracy

I've been struggling with learning cone 6 oxidation glazes since buying my L&L last spring. I've been using the MC6 schedule but have some pinholing in the licorce recipe and would like to try another firing schedule (and try thinning the glazes.)  I was reading Steven Hill's article and thought I was missing something when I read that he cooled naturally to 1700 so I searched the Internet. Thanks for posting June!  How did the tests turn out?  I thought I'd first try the SH probably schedule for bisque from the OR newsletter.  

You're welcome Karen! We tested some of them in soda but the kiln didn't get up to temperature, so when I can get around to it, I'll test them in my soda test kiln.

We're been dealing with a very serious health issue at our house, so I haven't even been able to get into the studio for 5 weeks or more.

Warmest regards,

June

I'm sorry to hear that June.  I send good thoughts and wishes for strength and healing of the health issues in your family. 

Karen

Thanks Karen. It will be a while before I can get back to work - how long I don't know. My husband is very weak and can't be left alone. We're hoping that he will rebound from the result of his treatments but it is going to take a while for his strength to return.

June

If you go to frogpondpottery.com you will see variations of the licorice glaze (called Ron's Black) and there is also one ones on masteringglazes.com that addressed crawling.  You can also try bisque firing higher.  You can also change the Whiting with Wollastonite (whiting causes pinholing).

http://ceramicartsdaily.org/firing-techniques/electric-kiln-firing/...

This has Steven Hill's firing schedule.

I purchased his video.  It is well worth the $50.  It has a thorough explanation of the method.  It also has his recipes.  Steven is very friendly and has sent me updated recipes as well as spent time talking on the phone with me with questions I have had.

He encourages you to try testing your current cone 6 glazes by spraying them over Strontium Crystal Magic to see what happens.

Contrary to what someone else commented it is not a slow fire.

Here is the schedule from his article in Ceramics Monthly:

RAMP 1: 200' F/hr. > 220'F  HOLD 1-3 HRS. depending on wetness of work

RAMP 2: 100' F/HR. > 500'F  HOLD: 0

RAMP 3: 400-500' F/HR .>2100'F  HOLD: 0

RAMP 4: 100'F > 2160- 2190'F HOLD for 30-60 minutes depending on kiln. This is Cone 5 and the hold will get you to Cone 6.  Test your kiln to find the correct hold time to achieve Cone 6.

RAMP 5: 9999'F /HR. >1700'F  This is for SKUTT kilns.  L&R should program 4000'F/HR.  HOLD: 0

RAMP 6: 50'F/HR. > 1600'F  HOLD 45-60 MINUTES

RAMP 7 50'F /HR. >1500'F HOLD: 0

I hope this helps.

Steven Hills Cone 6 Firing Schedule

200F/hr(ramp) to 220, Hold=0

400F/hr(ramp) to 2100, Hold=0

100F/hr(ramp) to 2170, Hold=60 min

Freefall to 1700, Hold=0

50/hr(ramp) to 1600, Hold=60

50/hr(ramp) to 1500, Hold=0

Kiln Off and let cool naturally

Depending on Age of Kiln you might have to tweak schedule. Use Cone Packs to understand how your kiln is firing and what temps your particular kiln reaches using this schedule. Cone 6 cone should be down.

I think it is important to stress the hold at Cone 5, it will fall between 30 and 60 minutes, rather than a set "60 minutes", each kiln is different and newer kilns with better insulation will take shorter to reach Cone 6 during that hold.  Obviously using some cone packs (^5,6,7)during the test run/runs will help determine the appropriate hold  time (as Brian noted in his reply).

Also Steven does a single firing of his pieces, so the Hold at at Ramp 1 is critical for this.  IF you are firing work that has already been Bisque fired, then the hold at RAMP 1 is probably not necessary, though a short hold isn't a bad thing.

I just reprinted the information from the Steven Hill article.  I have used this schedule with great success.

To make that Freefall happen at RAMP five,  Skutt temp is 9999'F and L&R is 4000/Hr.

Here's the schedule Steven posted on Facebook in 2010 right after he nailed it - don't know if he made any subsequent modifications or not...

"... briefly... cooled naturally to 1750, 50 an hour to 1600, 1 hour soak at 1600, 50 to 1500, then off. Pretty radical, but the micro crystalline glazes were spectacular!"

 

Karen - We normally use a 50F cooling between 1,800F and 1,500F, both with and without SCM. We lose the shiny poster-paint gloss which many ^6 glazes otherwise exhibit.

But we also get so much more crystallization that I need to add additional frit or other glass formers to typical ^6 glazes (used without SCM) to prevent them from "drying up" and turning matte during the crystallization.

I'm curious what is the main difference you see when you also hold at 1,600F for an hour? You say micro-crystalline formation, rather than macro-crystalline formation like the photo below. Or is this what you mean?

This is typical.  Clear Base Blue, glaze #39 on this webpage:

http://www.wpapotters.blogspot.com/2010/11/cone-6-oxidation-results...

Without a slow-cool, . . . with our slow-cool, . . . and finally the same glaze at our slow-cool with 10% 3269 Ferro Frit added.

Slow-cooling creates so much micro-crystallization that the shiny blue glaze becomes a matt brown. Adding frit enables the increased micro-crystallization to remain under a layer of glass - or at least that's my current explanation.

Karen Totten said:

Here's the schedule Steven posted on Facebook in 2010 right after he nailed it - don't know if he made any subsequent modifications or not...

"... briefly... cooled naturally to 1750, 50 an hour to 1600, 1 hour soak at 1600, 50 to 1500, then off. Pretty radical, but the micro crystalline glazes were spectacular!"

 

RSS

Videos

  • Add Videos
  • View All

Use These Links to Support Us

Low cost flat lapping disc can be used on you potters wheel if you, drill bat pin holes in it, and provide a trickle of water to cool it. At amazon.com, 120 grit for aggressive material removal. Click the image to purchase 

Members have had great things to say about John Britt's new book, Mid-Range Glazes. Click the image to buy from Amazon.com

Purchase Glazes Cone 6 by Michael Bailey, The Potters Book of Glaze Recipes by Emmanuel Cooper, or Making Marks by Robin Hopper, all available at amazon.comMastering Cone 6 Glazes by John Hesselberth & Ron Roy is now out of print.

Harbor Freight is a great place to find unbeatable prices for better HVLP spray guns with stainless steel parts and serviceable economy models, as well as detail guns, all tested by our members for spraying glazes, as well as compressors to power the guns. As yet no one has tested and commented on the remarkably inexpensive air brushes at harbor freight.

The critter siphon gun is a spray alternative that is well liked by some of our members, and is available at amazon.

Amazon is also a competitive source for photo light tents for shooting professional quality pictures of your work. They also have the EZ Cube brand favored by several of our members. You might also want to purchase the book Photographing Arts, Crafts and Collectibles . . .

If you are up to creating videos of your work or techniques you might want to invest in a flip video camera

Following are a few scales useful for potters. Ohaus Triple Pro Mechanical Triple Beam Balance, 2610g x 0.1g, with Tare $169.00

And finally a low cost clone of the OHaus. The Adam Equipment TBB2610T Triple Beam Mechanical Balance With Tare Beam $99.62

ebay is a great alternative for many tools and the equipment used in the ceramics studio - kilns, wheels, extruders, slab rollers are often listed there both new and used.

Tips for Members

If you just want to spout off, it is best accomplished as a blog posting. If you want to get more guidance and ideas from other members, ask a question as a new discussion topic. In the upper right corner of the lists for both types of posting, you will find an "+Add " button. Clicking it will open an editor where you create your posting. 4/16/2014

© 2024   Created by Andrea Wolf.   Powered by

Badges  |  Report an Issue  |  Terms of Service