Does anyone know what a good specific gravity is for VC satin matte? Also how much Bentonite is too much? I put 2% in this glaze and it is still hard panning. Do I add another 1% or try something else?

Views: 788

Reply to This

Replies to This Discussion

Robin -- Val Cushing Satin Matte is a "magnesium matte glaze" so adding more bentonite like Veegum is not likely to change the chemistry, until you get to the point there's enough magnesium to cause crawling in the glaze. - See the comparison below with 5% bentonite.

Bentonite is mostly silica (in a five to one ratio with alumina) with magnesium and/or calcium.

The 6 to 1 Silica to Alumina ratio of Bentonite is typical for a transparent glaze, which is what makes it an ideal additive. Kaolin is a ratio of only two parts silica to one part alumina, so adding more kaolin without also adding more silica would change the character of the glaze. The magensium in bentonite does denature low-fire cadmium sulfide reds, turning them black.

With only 10% clay there's not really enough to keep the whiting, frit and silica suspended. The feldspar you use may also leak sodium and potassium over time. In addition to adding bentonite you may want to try adding calcium chloride (ice melt crystals) to help the limited amount of clay maintain its suspension. Adding Epsom salts (magnesium sulfate) may add to the magnesium level enough to leave you with a crawling glaze.

Hi Norm

The recipe I used is as follows: Whiting 20, Frit 3124 - 25, Neph Sye 25, EPK 15, Silica 15, Zircopax 10

I made a 5000g batch, I may have screwed it up. I had added 2% Bentonite, that did nothing, so then I added some Epsoms Salts. For now it seems suspended. Hopefully it won't crawl. I wish I new more about the chemistry. If crawling does happen how can I fix it, if at all?

Robin - Nepheline Syenite is a notorious source of free sodium and potassium ions which cause a glaze to hard-pan. 

You get an flush of these atoms as the water leeches them from the particles of nepheline syenite -. and an ongoing source of sodium and potassium as bacterial action breaks down this raw material further.

This is far less of a problem when using other feldspars.  All glaze containing a big percentage of nepheline syenite will hard-pan over time, even if they contain 20% clay. Sodium and potassium ions make a conductive electrolyte which neutralize the charges on clay particle which make them repel each other.

The easy solution to your problem is the addition of calcium chloride, or epsom salts to flocculate the 15% clay (EPK). 

When you buy a deflocculant like Darvan or Sodium Silicate, they work by locking up calcium and magnesium ions and replacing them with a sodium ion. So these two flocculants add back the calcium or magnesium ions normally present in most water.

The recipe you're using is a calcium semi-matte which has for some reason been fluxed way down, I'd guess, to a Cone much lower than Cone 6. I bet you could get a nearly identical look with half as much zircopax. Zircopax is somewhat refractory, so at 10% that may explain all the low temperature fluxes flux used.  The added bentonite will not have changed the fired look of the glaze at all as the chemistry either way is almost identical.

Just add a tablespoon of calcium chloride or epsom salts to the bucket.  Of course you'll still need to use manual force with a scraper to pull this glaze off the bottom of the bucket and get these new ions mixed with it.

Thank you Norm, your information and explanations are invaluable!!  I added the epsom salts, all is nicely suspended and silky smooth. I'll be sure to let you know how it fires.

Reply to Discussion

RSS

Videos

  • Add Videos
  • View All

Use These Links to Support Us

Low cost flat lapping disc can be used on you potters wheel if you, drill bat pin holes in it, and provide a trickle of water to cool it. At amazon.com, 120 grit for aggressive material removal. Click the image to purchase 

Members have had great things to say about John Britt's new book, Mid-Range Glazes. Click the image to buy from Amazon.com

Purchase Glazes Cone 6 by Michael Bailey, The Potters Book of Glaze Recipes by Emmanuel Cooper, or Making Marks by Robin Hopper, all available at amazon.comMastering Cone 6 Glazes by John Hesselberth & Ron Roy is now out of print.

Harbor Freight is a great place to find unbeatable prices for better HVLP spray guns with stainless steel parts and serviceable economy models, as well as detail guns, all tested by our members for spraying glazes, as well as compressors to power the guns. As yet no one has tested and commented on the remarkably inexpensive air brushes at harbor freight.

The critter siphon gun is a spray alternative that is well liked by some of our members, and is available at amazon.

Amazon is also a competitive source for photo light tents for shooting professional quality pictures of your work. They also have the EZ Cube brand favored by several of our members. You might also want to purchase the book Photographing Arts, Crafts and Collectibles . . .

If you are up to creating videos of your work or techniques you might want to invest in a flip video camera

Following are a few scales useful for potters. Ohaus Triple Pro Mechanical Triple Beam Balance, 2610g x 0.1g, with Tare $169.00

And finally a low cost clone of the OHaus. The Adam Equipment TBB2610T Triple Beam Mechanical Balance With Tare Beam $99.62

ebay is a great alternative for many tools and the equipment used in the ceramics studio - kilns, wheels, extruders, slab rollers are often listed there both new and used.

Tips for Members

If you just want to spout off, it is best accomplished as a blog posting. If you want to get more guidance and ideas from other members, ask a question as a new discussion topic. In the upper right corner of the lists for both types of posting, you will find an "+Add " button. Clicking it will open an editor where you create your posting. 4/16/2014

© 2024   Created by Andrea Wolf.   Powered by

Badges  |  Report an Issue  |  Terms of Service